Warren Paint & Color Co. - Swimming Pool Paints

Unit of Measure

Items	700 Tropical White Swimming Pool Paint	NE 4085/ E 4005 White Polyamide High Gloss Epoxy Two Component Epoxy.	1584 Tropical White Swimming Pool Paint
Features	N/A Excellent Water Resistance Ideal for Concrete Pools and other Masonry Surfaces Semigloss Finish	N/A Excellent Corrosion and Chemical Resistance Free of Soluble Heavy Metals High Performance	N/A Excellent Water Resistance Ideal for Concrete Pools and other Masonry Surfaces Semigloss Finish
Surface Preparation	N/A Remove all dirt, scale, and grease. Concrete surfaces should be etched with muriatic acid diluted with water (1:4), rinsed thoroughly, and allowed to dry. Swimming pools should be washed with a detergent solution prior to acid etching to remove oils. Epoxies must be removed prior to application of this coating for underwater use. Underwater surfaces must be bone dry prior to application. Test for moisture by taping clear plastic film to the surface to be painted and observing for condensation after four hours.	N/A Remove all dirt, scale, and grease. Sand blast steel to SSPC-SP 6, Commercial Blast, and prime with P7387 Polyamide Epoxy Primer for best results. Concrete surfaces may be etched with muriatic acid diluted with water (1:10), rinsed thoroughly, allowed to dry, and neutralized with dilute baking soda, ammonia, or garden lime. Swimming pools should be washed with a detergent solution prior to acid etching to remove oils. Omit acid etching if pH of concrete of 7 or above cannot be verified by litmus test or other means.	N/A Remove all dirt, scale, and grease. Concrete surfaces should be etched with muriatic acid diluted with water (1:4), rinsed thoroughly, and allowed to dry. Swimming pools should be washed with a detergent solution prior to acid etching to remove oils. Epoxies must be removed prior to application of this coating for underwater use. Underwater surfaces must be bone dry prior to application. Test for moisture by taping clear plastic film to the surface to be painted and observing for condensation after four hours.
Mixing and Thinning	N/A Stir or shake well. Thin up to 10% with S 3, VM&P Naphtha; or another recommended thinner to spray. Use as supplied to brush or roll. Do not over-thin.	N/A Stir or shake well. Mix one part of NE 4085 White Polyamide High Gloss Epoxy one part E 4005 Epoxy Activator. Mix with power mixer or by hand for five minutes. Thin up to 20% with T 5932 Epoxy Reducer to spray. Pot life is four to five hours depending on temperature.	N/A Stir or shake well. Thin up to 10% with S 3, VM&P Naphtha; or another recommended thinner to spray. Use as supplied to brush or roll. Do not over-thin.
Application	N/A Brush, roll, spray. Thin as directed for conventional or H.V.L.P. spray. Apply between 50 and 95°F with the relative humidity less than 80%. Do not expose to water within four hours after painting.	N/A Brush, roll, or spray. Thin as directed for conventional or H.V.L.P. spray. Apply between 50 and 90°F with the relative humidity less than 80%. Do not expose to dew or rain within eight hours after painting. Humidity can exceed 80% and dry times can be shortened if heat (no more than 300ºF) is applied soon after application. Full resistance properties are developed within seven days.	N/A Brush, roll, spray. Thin as directed for conventional or H.V.L.P. spray. Apply between 50 and 95°F with the relative humidity less than 80%. Do not expose to water within four hours after painting.
Dry Time	N/A One hour to touch. Eight hours until use or traffic is allowed. Forty-eight hours before immersion.	N/A One hour to touch. Three hours to handle. Twelve hours hard	N/A One hour to touch. Eight hours until use or traffic is allowed. Forty-eight hours before immersion.
Recoat Time	N/A After one hour.	N/A Between 12 and 48 hours. After 48 hours, a light sanding is recommended before recoat.	N/A After one hour.
Appearance	N/A Semi-gloss white film	N/A High gloss white film.	N/A Semi-gloss white film.
Composition	N/A Titanium dioxide.	N/A Titanium dioxide and calcium carbonate	N/A Titanium dioxide.
Vehicle	N/A Vinyl toluene acrylate copolymer and tung oil reduced with high ?ash naphtha and mineral spirits.	N/A Polyamide epoxy thinned with xylene, secondary butyl alcohol, and MIBK	N/A Vinyl toluene acrylate copolymer and tung oil reduced with high ?ash naphtha and mineral spirits.
% Solids by Weight	N/A 51.7	N/A 67.5	N/A 51.7
% Solids by Volume	N/A 38.6	N/A 53.9	N/A 38.6
Coverage	N/A 413 square feet per gallon at 1.5 mils DFT (100% transfer and Zero profile).	N/A 216-432 square feet per gallon at a recommended 2.0-4.0 mils DPT (100% transfer and Zero profile).	N/A 413 square feet per gallon at 1.5 mils DFT (100% transfer and Zero profile).
V.O.C.	N/A 4.42 LB/gal	N/A 3.21 lb/gal for parts A and B mixed 1:1.	N/A 4.2 LB/gal
Cured Film Properties	N/A Excellent water resistance within 48 hours. Good resistance to aliphatic solvents and many oils within 48 hours.	N/A Excellent anticorrosive properties over steel. Very good water resistance within eight hours. Good resistance to solvents and chemicals within seven days. Not designed as an exterior finish coat.	N/A Excellent water resistance within 48 hours. Good resistance to aliphatic solvents and many oils within 48 hours.
Standard Packaging	N/A One gallon cans (packaged four per case). Fives and drums are available by special order.	N/A Two gallon kit , packaged four gallons per case. Fives and drums are available by special order.	N/A One gallon cans (packaged four per case). Fives and drums are available by special order.