Item # NE 4085 / E 4005, White Polyamide High Gloss Epoxy Two Component Epoxy



Warren's White Polyamide High Gloss Epoxy is formulated to provide extreme resistance to corrosion, acids, alkalis, solvents, and other chemicals. It may be used in a marine environment for long term protection of steel and concrete. Neva-Rust is a low-temperature cure surface tolerant epoxy coating for steel structures that provides extreme performance. White Polyamide High Gloss Epoxy is available in white and gray with high build, semi-gloss, and special colors available by special order.




 Specifications   

Features

High Performance
Excellent Corrosion and Chemical Resistance
Free of Soluble Heavy Metals

Surface Preparation

Remove all dirt, scale, and grease. Sand blast steel to SSPC-SP 6, Commercial Blast, and prime with P7387 Polyamide Epoxy Primer for best results. Concrete surfaces may be etched with muriatic acid diluted with water (1:10), rinsed thoroughly, allowed to dry, and neutralized with dilute baking soda, ammonia, or garden lime. Swimming pools should be washed with a detergent solution prior to acid etching to remove oils. Omit acid etching if pH of concrete of 7 or above cannot be verified by litmus test or other means.

Mixing and Thinning

Stir or shake well. Mix one part of NE 4085 White Polyamide High Gloss Epoxy one part E 4005 Epoxy Activator. Mix with power mixer or by hand for five minutes. Thin up to 20% with T 5932 Epoxy Reducer to spray. Pot life is four to five hours depending on temperature.

Application

Brush, roll, or spray. Thin as directed for conventional or H.V.L.P. spray. Apply between 50 and 90ºF with the relative humidity less than 80%. Do not expose to dew or rain within eight hours after painting. Humidity can exceed 80% and dry times can be shortened if heat (no more than 300ºF) is applied soon after application. Full resistance properties are developed within seven days.

Dry Time

One hour to touch. Three hours to handle. Twelve hours hard

Recoat Time

Between 12 and 48 hours. After 48 hours, a light sanding is recommended before recoat.

Appearance

High gloss white film.

Composition

Titanium dioxide and calcium carbonate.

Vehicle

Polyamide epoxy thinned with xylene, secondary butyl alcohol, and MIBK.

% Solids by Weight

67.5

% Solids by Volume

53.9

Coverage

216-432 square feet per gallon at a recommended 2.0-4.0 mils DFT (100% transfer and zero profile).

V.O.C.

3.21 lb/gal for parts A and B mixed 1:1.

Cured Film Properties

Excellent anticorrosive properties over steel. Very good water resistance within eight hours. Good resistance to solvents and chemicals within seven days. Not designed as an exterior finish coat.

Standard Packaging

Two gallon kit, packaged four gallons per case. Fives and drums are available by special order.